Mg2Nni0.5Co0.5compound obtaining by mechanical alloying and their performance on hydriding process

Título traducido de la contribución: Obtención del compuesto Mg2Ni0.5Co0.5mediante aleado mecánico y estudio de su comportamiento frente al proceso de hidruración

Carola Martínez, Stella Ordoñez, Danny Guzmán, Daniel Serafini, Paula Rojas, Claudio Aguilar

Producción científica: Contribución a una revistaArtículorevisión exhaustiva

Resumen

This work presents the microstructural evolution of mechanically alloyed Mg2Ni0.5Co0.5and a study of its hydriding properties. Mg, Ni, and Co elemental powders (atomic ratios of 2:0.5:0.5, respectively) were mechanically alloyed in a Spex 8000D high-energy mill for 36 h (amorphous sample) and subsequently submitted to a thermal treatment at 673 K for 15 min (nanocrystalline sample). The characterizations of the samples were performed with X-ray diffraction. A Sievert-type volumetric hydriding process was done at 363 K and with hydrogen pressure of 2 MPa. Desorption process was evaluated through differential scanning calorimetry. Based on the obtained results, it is possible to conclude that the amorphous structure absorbs more hydrogen, reaching a maximum of 3.6 wt. % H. Desorption process events depend on amorphous or nanocrystalline states.

Título traducido de la contribuciónObtención del compuesto Mg2Ni0.5Co0.5mediante aleado mecánico y estudio de su comportamiento frente al proceso de hidruración
Idioma originalInglés
Páginas (desde-hasta)240-246
Número de páginas7
PublicaciónDYNA (Colombia)
Volumen84
N.º200
DOI
EstadoPublicada - 2017
Publicado de forma externa

Huella

Profundice en los temas de investigación de 'Obtención del compuesto Mg2Ni0.5Co0.5mediante aleado mecánico y estudio de su comportamiento frente al proceso de hidruración'. En conjunto forman una huella única.

Citar esto