Microstructure and magnetic properties of Cu_90−xCo₁₀Ni_x–7.5% SmCo₅ composite alloys prepared by mechanical alloying and hot pressing

Keyphrases

• Mechanical Alloying 100%
• Hot Pressing 100%
• Microstructure Properties 100%
• Magnetic Properties 100%
• Composite Alloy 100%
• SmCo5 100%
• Intermetallics 60%
• Reinforced 40%
• Pure Ni 20%
• Argon Atmosphere 20%
• Planetary Mill 20%
• Milling Process 20%
• Scanning Electron Microscopy 20%
• Cu-Ni 20%
• X-ray Diffraction Method 20%
• Processing Stages 20%
• Oxides 20%
• Alloy Powder 20%
• Cu-Co 20%
• Electron Probe Microanalyzer 20%
• Powder Alloys 20%
• Pure Cu 20%
• Nanocrystalline Composite 20%
• Second Phase Particles 20%

INIS

• microstructure 100%
• alloys 100%
• hot pressing 100%
• magnetic properties 100%
• powders 60%
• particles 60%
• intermetallic compounds 60%
• milling 40%
• argon 20%
• processing 20%
• atmospheres 20%
• x-ray diffraction 20%
• production 20%
• scanning electron microscopy 20%
• pressure range mega pa 20%
• compacts 20%
• synthesis 20%
• fabrication 20%
• oxides 20%
• precipitation 20%
• diffraction methods 20%
• electron microprobe analysis 20%

Material Science

• Powder 100%
• Mechanical Alloying 100%
• Hot Pressing 100%
• Intermetallics 100%
• Magnetic Property 100%
• X-Ray Diffraction 33%
• Scanning Electron Microscopy 33%
• Oxide Compound 33%
• Electron Microprobe 33%
• Nanocrystalline Composite 33%