High-Yield Synthesis of Poly(3-hydroxybutyrate- co-3-hydroxyvalerate) Copolymers in a Mixed Microbial Culture: Effect of Substrate Switching and F/M Ratio

Tania Palmeiro-Sánchez, Angeles Val Del Rio, Andrea Fra-Vázquez, José Luis Campos, Anuska Mosquera-Corral

Producción científica: Contribución a una revistaArtículorevisión exhaustiva

13 Citas (Scopus)

Resumen

The accumulation capacity of a mixed microbial culture (MMC) is affected if the substrate used in the accumulation experiments differs from the one used in the enrichment. For this reason, the effect of substrate switching was studied to determine the versatility of an MMC enriched in a mixture of volatile fatty acids (VFAmix) to overcome this problem. The MMC was enriched using a VFAmix composed of 48.3:24.3:7.3:14.7 CmM acetic (HAc), propionic (HPr), butyric (HBu), and valeric (HVa) acids, respectively. The accumulation capacity was tested using single VFAs (HAc, HPr, HBu, and HVa), as well as the VFAmix used in the enrichment. The accumulation capacities were 52.8 ± 4.7, 48.8 ± 4.3, 45.2 ± 3.0, 48.4 ± 1.0, and 54.5 ± 8.0 wt% for HAc, HPr, HBu, HVa, and VFAmix, respectively, with polymer compositions of 50.6 ± 15.1, 0.4 ± 0.1, 63.2 ± 1.5, 0.3 ± 0.0, and 2.0 ± 0.7 g 3-HB/g 3-HV, following the same order. The average yields were 0.84 ± 0.08, 0.76 ± 0.09, 0.74 ± 0.02, 0.70 ± 0.01, and 0.68 ± 0.09 CmolPHA/CmolVFA for HVa, VFAmix, HAc, HBu, and HPr, respectively. The feed-to-microorganism (F/M) ratio showed that values of 1-7 CmolVFA/(CmolX) in the accumulation experiments led to the optimal yields. Based on the results obtained, it seems feasible to enrich an MMC able to produce tailor-made biopolymers from different VFAs at high yields.

Idioma originalInglés
Páginas (desde-hasta)21921-21926
Número de páginas6
PublicaciónIndustrial and Engineering Chemistry Research
Volumen58
N.º48
DOI
EstadoPublicada - 4 dic. 2019
Publicado de forma externa

Huella

Profundice en los temas de investigación de 'High-Yield Synthesis of Poly(3-hydroxybutyrate- co-3-hydroxyvalerate) Copolymers in a Mixed Microbial Culture: Effect of Substrate Switching and F/M Ratio'. En conjunto forman una huella única.

Citar esto