Caracterizacion microestructural de las aleaciones base cobre Cu 95Co5 y Cu90Co5Ni5 obtenidas por aleado mecanico y sinterizacion

Marta López, Valentina Ortiz, María E. Gómez, David Reyes, Ramalinga Mangalaraja, Pedro Prieto, José Jiménez

Resultado de la investigación: Contribución a una revistaArtículorevisión exhaustiva

Resumen

The magneto-resistant properties of nanostructured Cu95Co 5 y Co90Co5-Ni5 alloys show their interesting in candidature for multiple applications. The alloys were obtained by mechanical alloying using a planetary mill with rotational speed of 155rpm under argon atmosphere for 30, 45 and 60h as milling time. The magnetic properties obtained at 300K as a function of milling time reveals that the Cu-Co-Ni alloys show super-paramagnetism behaviour. The XRD analysis indicates that the Ms decreasing is due to the reduction copper oxide and Co structural changes from Co-fcc to Co-hc. An additional strengthening on the grain structure by alloys consolidation have the formation of CuNi solid solutions and precipitations of magnetic domains Co nanoparticles under 1nm in grain size. The SEM observation of CuCoNi alloys with the comparison of CuCo alloys shows the less phase segregation and it is attributed to the complete solubility of Ni in copper.

Título traducido de la contribuciónMicrostructural characterization of Cu95Co5 and Cu90Co5Ni5 copper-based alloys obtained through mechanical alloy and synthesization
Idioma originalEspañol
Páginas (desde-hasta)141-148
Número de páginas8
PublicaciónRevista Latinoamericana de Metalurgia y Materiales
Volumen30
N.º2
EstadoPublicada - 2010
Publicado de forma externa

Palabras clave

  • Characterization
  • Granular nanomaterials
  • Magnetic copper material

Huella

Profundice en los temas de investigación de 'Caracterizacion microestructural de las aleaciones base cobre Cu 95Co5 y Cu90Co5Ni5 obtenidas por aleado mecanico y sinterizacion'. En conjunto forman una huella única.

Citar esto