Análisis de perfiles de difracción de rayos X de una aleación Cu-8% en peso de Cr obtenida por medio de aleado mecánico

C. Aguilar, P. A. Rojas, S. Ordoñez, D. Guzman

Producción científica: Contribución a una revistaArtículorevisión exhaustiva

4 Citas (Scopus)

Resumen

This work studies the evolution of the microstrucutre of a mechanically alloyed Cu-8 wt. % Cr powder mixture by X-Ray profiles analysis. The process was carried out using a SPEX8000D upon mix with stainless steels containers and balls, keeping a constant powder to balls weight ratio of 10. Increasing the milling time, crystallite size and stacking fault energy decreased and microstrain and stacking fault probability increased. The crystallite size distribution shifts to lower crystallite size values by increasing the milling time. After a milling time of 50 hours, the data showed that a solid solution of chromium in copper was produced.

Título traducido de la contribuciónX-Ray profile analysis of Cu-8wt.%Cr processed by mechanical alloying
Idioma originalPortugués
Páginas (desde-hasta)777-786
Número de páginas10
PublicaciónRevista Materia
Volumen14
N.º2
DOI
EstadoPublicada - 2009

Huella

Profundice en los temas de investigación de 'Análisis de perfiles de difracción de rayos X de una aleación Cu-8% en peso de Cr obtenida por medio de aleado mecánico'. En conjunto forman una huella única.

Citar esto